FREEZE-THAW AND FIRE RESISTANCE OF GEOPOLYMER MORTAR BASED ON NATURAL AND WASTE POZZOLANS
 
Degirmenci F.Nurhayat
 
Balikesir University, Architecture Faculty, Department of Architecture, Cagis campus, 10145, Balikesir, Turkey

Keywords: Fly ash, Ground granulated blast furnace slag, Natural zeolite, Alkaline activator solution
 

The purpose of this research was to investigate the resistance of pozzolan-based geopolymer mortars subjected to high temperatures and freeze-thaw cycles. Low calcium fly ash and granulated blast furnace slag as waste pozzolans and natural zeolite as a natural pozzolan were used as base materials for producing geopolymer mortar. The other purpose the research was to study the effect of alkaline activator ratio (Na₂SiO₃/NaOH) on the performance of pozzolan-based geopolymer mortar specimens subjected to extreme temperatures. The influence of high temperatures on the properties of mortars was investigated at 300°C, 600°C, and 900°C. Fire and freeze-thaw and resistance of mortars were investigated in terms of visual appearance, weight loss and residual compressive strength. The minimal values of the residual compressive strength were obtained at 900°C for all mixtures. The residual compressive strength of all specimens was lower than the values obtained for specimens not subjected to any freeze-thaw resistance test, except those containing GGBS. The Na₂SiO₃/NaOH ratios of the alkaline activator solution used to prepare the geopolymer mortars have an effect on the weight losses and residual compressive strengths of the specimens subjected to high temperatures and freeze-thaw cycles. As the Na2SiO3/NaOH ratios increased, the weight and strength losses decreased.


PDF (1.8 MB)

doi: 10.13168/cs.2017.0043
 
 
Licence Creative Commons © 2015 - 2019
Institute of Rock Structure and Mechanics AS CR, v.v.i. & University of Chemistry and Technology, Prague
Webmaster | Journal Contact