THERMAL PROPERTIES AND HOMOGENITY RANGE OF Bi24+xCo2-xO39 CERAMICS
 
Jankovský O. 1, Sedmidubský D. 1, Sofer Z. 1, Čapek J. 2, Růžička K. 3
 
1 Department of Inorganic Chemistry, Institute of Chemical Technology Prague, Technicka 5, 166 28 Prague 6, Czech Republic
2 Department of Metals and Corrosion engineering, Institute of Chemical Technology Prague, Technicka 5, 166 28 Prague 6, Czech Republic
3 Department of Physical Chemistry, Institute of Chemical Technology Prague, Technicka 5, 166 28 Prague 6, Czech Republic

Keywords: Cobalt sillenite, Thermal properties, Heat capacity
 

Samples with different Bi2O3/Co2O3 ratio were prepared by ceramic route. Based on the results of DTA, XRD and SEM – EDX a section of phase diagram of the Bi–Co–O diagram in air atmosphere was calculated using the FactSage software. The sillenite structure of Bi24+xCo2-xO39 was confirmed and described. The Rietveld analysis confirmed SEM – EDX results. The heat capacity and enthalpy increments of Bi24Co2O39 were measured by differential scanning calorimetry (DSC) from 258 K to 355 K and by the drop calorimetry from 573 K to 973 K. Above room temperature the temperature dependence of the molar heat capacity in the form Cpm = (1467.87 + 0.299410 · T – 15888378 · T-2) J K-1 mol-1 was derived by least-squares method from the experimental data.