THE EFFECT OF SURFACE ACTIVE SUBSTANCE CONCENTRATION ON THE PROPERTIES OF FOAMED AND NON-FOAMED GYPSUM
 
Bazelová Zora, Pach Ladislav, Lokaj Ján
 
Department of Ceramics, Glass and Cement, Faculty of Chemical and Food Technology, Slovak Technical University, Radlinského 9, Bratislava, Slovakia

Keywords: Foamed gypsum, Surfactant, Ceramic, Bulk Density, Compressive strength
 

Foamed gypsum was prepared by the direct foaming method. Properties of foamed and non-foamed gypsum were investigated using plaster suspension containing surface active substance (SAS). Since SAS has amphiphilic properties its solutions are prone to foaming. The combination of foaming and the hydration of calcium sulphate hemihydrate (CaSO₄,1/2H₂O) led to fast solidification, resulting in strong, porous bodies. Bulk density, compressive strength and the pore size varied markedly depending on both the quantity of SAS and water/plaster weight ratio. Bulk density of the foamed gypsum ranged from 0.20 to 0.58 g/cm³ and the pore size reached 50 µm to 1.3 mm depending on the concentration of the surfactant. The compressive strength of the foamed gypsum and the non-foamed one increased with increasing bulk density. The dried non-foamed gypsum showed high compressive strengths up to 12 MPa.


PDF (2.7 MB)
 
Licence Creative Commons © 2015 - 2024
Institute of Rock Structure and Mechanics of the CAS & University of Chemistry and Technology, Prague
Webmaster | Journal Contact