EFFECT OF SILICA FUME AND METAKAOLINE POZZOLANA ON THE PERFORMANCE OF BLENDED CEMENT PASTES AGAINST FIRE
 
Morsy Mohamed S., Shebl Sayed S.
 
Housing and Building Research Center, P. O. Box 1770, Cairo, Egypt

Keywords: Metakaoline, Silica fume, Portland cement, Thermal stability, Thermal shock resistance, Compressive strength, DSC
 

The aim of this investigation is to study the effect of the subsititution of metakaoline (MK) by silica fume (SF) upon the thermal stability of Portland cement -MK blended pastes. The kaoline was thermally activated at 850°C for 2 hours. The cement pastes were prepared with constant consistency. The pastes were kept in moulds at 20°C/100 % relative humidity for 24 hours and then hydrated for 28 days under water. The hydrated pastes were exposed for 2 hours to temperatures of 100, 200, 400, 600 and 800°C. The hydrated specimens were tested for compressive strength, thermal stability and phase composition after heat treatment. It was found that, after increase of compressive strength of control cement paste up to 200°C, the paste suffers a more loss of compressive strength with further increasing treatment temperatures. But, it was evidenced that the compressive strength of blended cements increases with temperature up to 400°C and then, it decreases as increase the treatment temperatures up to 800°C. The replacement of Portland cement (PC) by 15 % MK and 5 % SF in cement pastes increases the thermal shock resistance by about 10 times.


PDF (0.2 MB)
 
Licence Creative Commons © 2015 - 2024
Institute of Rock Structure and Mechanics of the CAS & University of Chemistry and Technology, Prague
Webmaster | Journal Contact