HLAVNÍ TECHNOLOGICKÉ CHARAKTERISTIKY SKLÁŘSKÝCH TAVICÍCH PROSTORŮ Z HLEDISKA PRŮBĚHU TAVICÍHO PROCESU

Část II. Hlavní charakteristiky do okamžiku rozpuštění písku

MAIN TECHNOLOGICAL CHARACTERISTICS OF GLASS TANK MELTING ZONES FROM THE STANDPOINT OF THE COURSE OF THE MELTING PROCESS

Part II. Main characteristics up to the moment of sand dissolving


 
Němec Lubomír 1, Laurentová Simona 2
 
1 Společná laboratoř pro chemii a technologii silikátů ČSAV a VŠCHT, 166 28 Praha 6 Suchbátarova 5
2 Katedra technologie silikátů VŠCHT, 166 28 Praha 6, Suchbátarova 5

1 Joint Laboratory for the Chemistry and Technology of Silicates, Czechoslovak Academy of Sciences and Institute of Chemical Technology, 166 28 Prague
2 Department of Silicate Technology, Institute of Chemical Technology, 166 28 Prague



S využitím teoretických podkladů z části I byl zjišťován vliv teploty tavení, zrnitosti písku, typu a koncentrace čeřiva, velikosti mrtvého prostoru a míchání taveniny probubláváním na měrnou spotřebu energie a výkon jednoduchého modelového tavicího prostoru při tavení sodno-vápenaté skloviny. Výsledky výpočtů ukázaly výrazně příznivý vliv vysoké tavicí teploty; k nepatrnému zvýšení měrné spotřeby energie dochází až při teplotách nad 1 500 - 1 550 °C. Rovněž vysoké využití tavicího prostoru je významným příznivým faktorem, především v oblasti středních a nižších teplot. Příznivé ovlivnění tavicích charakteristik ostatními faktory projevujícími se rovněž především v oblasti středních a nižších teplot je podmíněno snížením rozměru maximálního zrna písku, posunem granulometrie písku směrem k monodisperzi, nízkou koncentraci čeřiva (za podmínky vyčeření) a mícháním skloviny.

Investigation of the effect of basic factors, i.e. temperature, sand grain size, type and concentration of the refining agent, the size of the dead zone and glass melt stirring on the melting characteristics, i.e. specific energy consumption and throughput of the model melting zone, allows the trends leading to optimum values of the two characteristics to be determined. Using the theoretical data dealt with in Part I and experimental data on sand dissolution obtained earlier, characteristics were calculated for soda-lime glass and flat glass up to the moment sand has completely dissolved. The calculations provided evidence for the advantage of a high mean melting temperature which leads to lower energy consumption; the respective temperature dependence exhibits a minimum at a temperature corresponding to maximum temperatures in some modern glass tank zones. High temperature was also proved to have a favourable effect on the throughput of the melting zone. Another favourable factor appears to be high utilization of the melting zone, particularly at medium and lower mean melting temperatures. The other factors in question are of some significance also at medium and lower melting temperatures; the characteristics can be favourably affected by reducing the size of the largest sand grains, shifting the sand granulometry towards monodispersity, by a low concentration of the refining agent (which, however, should ensure adequate refining) and application of melt stirring.